| Presentation Title |
Process Robustness of Friction Stir Dovetailing of AA7099 to Steel with In Situ AA6061 Interlayer Linking |
| Author(s) |
Md Reza-E-Rabby, Timothy Roosendaal, Piyush Upadhyay, Nicole Overman, Joshua Silverstein, Martin McDonnell, Scott Whalen |
| On-Site Speaker (Planned) |
Md Reza-E-Rabby |
| Abstract Scope |
Rolled homogeneous armor (RHA) steel was joined to aluminum alloy AA7099-T7451 with an interlayer of AA6061-T651 by single-pass friction stir dovetailing (FSD). The evolution of the AA7099/AA6061 and AA6061/Steel interfacial microstructure and mechanical properties of the joints were examined. The AA6061 interlayer prevented Zn from migrating from the AA7099 to the steel during FSD and forming brittle, Zn-rich, Fe-Al intermetallic compounds within the joint. The flow of the dissimilar aluminum alloys at the interface was controlled with a partially threaded friction stir welding pin and a dovetail geometric configuration optimized in previous work. The process robustness was explored to establish parameter windows by elucidating parametric effects on the relationship between process conditions and the joint’s microstructure and mechanical properties. Ranges of process forge force (50–70 kN) and interface temperature (475°C–520°C) consistently yielded joints with adequate performance. The load-carrying capacity in lap shear tensile tests was 2100±100 N/mm. |
| Proceedings Inclusion? |
Planned: |