| Presentation Title |
Influence of Precoating on the Decarburization of the Surface Layer of Forged Parts during the Hot Die Forging Process |
| Author(s) |
Zbigniew Gronostajski, Pawel Widomski, Marcin Kaszuba, Maciej Zwierzchowski |
| On-Site Speaker (Planned) |
Pawel Widomski |
| Abstract Scope |
This research evaluates the effect of pre-coating of forged parts on decarburization. First, the effect of different coatings on the rods decarburization during the induction heating process was tested. Coatings were deposited before forging. Once completed testing, the measurements and observations of the decarbonized layer were made. The next stage involved analysis of the decarburization of the forged parts after forging. The forged parts were made using precoating of pre-forging elements; pieces cut off a metal rod. Based on tests results, the possibility of using this solution in the technique of industrial hot forging was evaluated. The results of laboratory tests have confirmed that lubrication of metal pieces is sufficient, as well as proved it to be effective in reducing decarburization of the surface layer. Results indicate that decarburization may be reduced to a minimum when we use Bonderite product in a concentration of 66% and 50%. |
| Proceedings Inclusion? |
Definite: At-meeting proceedings |